Ti6.5Al1Mo1V2Zr Powder
Ti6.5Al1Mo1V2Zr Powder
|
spherical Ti6.5Al1Mo1V2Zr powder is prepared by the plasma rotary electrode atomized process. Ti6.5Al1Mo1V2Zr alloy bar of end surface is heated by plasma arc to melt into liquid, and the liquid is ejected and crushed into fine droplets by the centrifugal force of high-speed rotation of the electrode. The droplets eventually form a spherical powder under the action of surface tension in the condensation process.
|
20-60um
|
45-105um
|
45-150um
|
PSD |
0-20um, 15-45um, 20-60um, 45-105um, 45-150um |
Purity |
0.999 |
Sphericity |
>95% |
Oxygen Content |
600-1500ppm |
Flow Ability |
13-25s/50g |
Standard |
ASTM B348, ASTM F136, ASTM F1580, ASTM F2924, ASTM F3001, AMS 1498 |
Particle Size Distribution Ti6.5Al1Mo1V2Zr Powder
Particle size distribution is measured by laser diffraction as per ASTM B822. Due to the Almost no satellite powder and hollow powder, high sphericity with excellent fluidity, low oxygen content on AM Co., Ltd. powder, the particle size distribution is highly uniform and the D10, D50 and D90 meet and exceed the industry requirements with an exceptional batch to batch reliability. The typical powder of plasma rotary electrode atomized process yield ranges from 0-150 µm, after atomization, the powder is sieved according customer specifications.