Stainless Steel Powder
SS Powder
|
Spherical Stainless Steel 316L powder is prepared by the plasma rotary electrode atomized process (PREP). The metal powder has low oxygen content, High sintering density, good mechanical properties, smooth surface and nearly spherical morphology improve the production difficulty of ultra-thin and ultra-small parts, and the free combination of particle size. Mainly used in powder metallurgy, plasma spraying, laser cladding, porous materials or as welding material additives
|
20-60um
|
45-105um
|
45-150um
|
Element |
Fe |
Cr |
Mo |
Mn |
Si |
Ni |
P |
O |
C |
Tested |
Bal |
16-18 |
43864 |
44118 |
≤1.5 |
44118 |
≤0.045 |
≤0.1 |
≤0.03 |
PSD |
0-20um, 15-45um, 20-60um, 45-105um, 45-150um |
Purity |
0.9999 |
Sphericity |
>95% |
Bulk Density |
4.00g/cm3 |
Tap Density |
4.69g/cm3 |
Flow Ability |
10-20s/50g |
Standard |
ASTM B348, ASTM F136, ASTM F1580, ASTM F2924, ASTM F3001, AMS 1498 |
Particle Size Distribution Stainless Steel 316L Powder
Particle size distribution is measured by laser diffraction as per ASTM B822. Due to the Almost no satellite powder and hollow powder, high sphericity with excellent fluidity, low oxygen content on AM Co., Ltd. powder, the particle size distribution is highly uniform and the D10, D50 and D90 meet and exceed the industry requirements with an exceptional batch to batch reliability. The typical powder of plasma rotary electrode atomized process yield ranges from 0-150 µm, after atomization, the powder is sieved according customer specifications.