Cobalt-Chromium Powder
CoCrMo Powder
|
Spherical CoCrMo powder is prepared by the plasma rotary electrode atomization process with good fluidity and almost no hollow powder, which widely used in medical implant.
Cobalt-chromium alloys have been widely used in oral, dental and surgical implants for the restoration of most teeth, especially for fixed restorations such as posterior fixed bridges.
|
20-60um
|
45-105um
|
45-150um
|
Element |
Co |
Cr |
Mo |
Si |
Mn |
Ni |
C |
Tested |
Bal |
26.5-30 |
4.5-7.0 |
1 |
≤1.00 |
≤1.00 |
≤0.35 |
PSD |
0-20um, 15-45um, 20-60um, 45-105um, 45-150um |
Purity |
0.9999 |
Oxygen Content |
<300 ppm |
Sphericity |
>95% |
Bulk Density |
4.2g/cm3 |
Flow Ability |
11-20s/50g |
Tensile Strength |
1100 +/-50MPa |
Yield Strength |
630 +/-50MPa |
Elongation |
9 +/-2% |
Application |
SLM/EBM, Laser Cladding, Spraying |
Standard |
ASTM B348, ASTM F136, ASTM F1580, ASTM F2924, ASTM F3001, AMS 1498 |
Particle Size Distribution Stainless Steel 316L Powder
Particle size distribution is measured by laser diffraction as per ASTM B822. Due to the Almost no satellite powder and hollow powder, high sphericity with excellent fluidity, low oxygen content on AM Co., Ltd. powder, the particle size distribution is highly uniform and the D10, D50 and D90 meet and exceed the industry requirements with an exceptional batch to batch reliability. The typical powder of plasma rotary electrode atomized process yield ranges from 0-150 µm, after atomization, the powder is sieved according customer specifications.